Study on the Mechanical Properties and Dispersion of LDPE/nano-CaCO3 Composites Prepared by Vane Extruder

【摘要】:Vane extruder is an innovative equipment for polymer processing.Researches have proved that compared with traditional screw extruder,this new facility have many outstanding characteristics such as shorter thermo-mechanical processing,lower unit consumption,better production performance.However,the effect of the vane extruder on the mechanical properties and dispersion of polymer/inorganic filler composites has not been studied.In this paper,low density polyethylene (LDPE)/nano-CaCO3 composites were prepared both by vane extruder and screw extruder.The different effects of these two extrusions on the mechanical properties and dispersion of the composites were explored using tensile test as well as scanning electron microscope (SEM) test.The tensile results showed that the mechanical properties of the composites is much better extruded by vane extruder than that by screw extruder:When the content of nano-CaCO3 is 8%,in the extrusion direction,tensile strength increases by 35% and elongation at break increases by 25%,while in the transverse direction,tensile strength by 15% and elongation at break by 10%.The SEM graphs indicated that based on extensional rheology,the extrusion of vane extruder has more excellent dispersion,which in turn illustrated the increase in the mechanical performance.

知网文化
【相似文献】
中国重要会议论文全文数据库 前10条
1 ;Study on the Mechanical Properties and Dispersion of LDPE/nano-CaCO3 Composites Prepared by Vane Extruder[A];2011中国材料研讨会论文摘要集[C];2011年
2 黄海友;聂铭君;栾燕燕;谢建新;;Fatigue Property of Cu-12wt%Al Alloys Fabricated by Continuous Unidirectional Solidification[A];2011中国材料研讨会论文摘要集[C];2011年
3 Joseph A.Abys;;Understanding Whisker Phenomenon:The Driving Force for Whisker Formation[A];2003年全国电子电镀学术研讨会论文集[C];2003年
4 ;Static Deformation Due to Shear and Tensile Faults in a Layered Half-Space[A];中国科学院地质与地球物理研究所二○○三学术论文汇编·第一卷(地球动力学)[C];2003年
5 ;Study on the Extensional Effect in the Conveying and Plasticizing Process of Vane Extruder[A];2011中国材料研讨会论文摘要集[C];2011年
6 ;Discussion of the paper“Stress state analysis of a collapsed overhanging rock slab:A case study”by P.Paronuzzi and W.Serafini,Engineering Geology,108:65-75(2009)[A];中国科学院地质与地球物理研究所第11届(2011年度)学术年会论文集(中)[C];2012年
7 C.A.Hsu;C.K.Hsieh;;Study on Radiographic Testing of Weld Nugget Defects in High Strength Steels[A];2010年海峡两岸材料破坏/断裂学术会议暨第十届破坏科学研讨会/第八届全国MTS材料试验学术会议论文集[C];2010年
8 ;Comment on“Weak tensile characteristics of loess in China-An important reason for ground fissures”by Ping Sun,Jian-bing Peng,Li-wei Chen,Yue-ping Yin,Shu-ren Wu[A];中国科学院地质与地球物理研究所第十届(2010年度)学术年会论文集(中)[C];2011年
9 J.F.Parr;;Preparation and properties of TiO_2 /fumed silica composite photocatalytic materials[A];2011中国材料研讨会论文摘要集[C];2011年
10 杜艳艳;卢一平;王同敏;;Effect of Electromagnetic Stirring on Microstructure and Properties of Al_(0.5)CoCrCuFeNi Alloy[A];2011中国材料研讨会论文摘要集[C];2011年
中国博士学位论文全文数据库 前3条
1 贾楠;对双相不锈钢微观形变行为的研究—原位实验与自洽模拟[D];东北大学;2008年
2 张双燕;化学成分对木材细胞壁力学性能影响的研究[D];中国林业科学研究院;2011年
3 岳永海;低维单体纳米材料原位变形方法及其力学行为的研究[D];北京工业大学;2012年
中国硕士学位论文全文数据库 前10条
1 宾诺德;[D];东华大学;2012年
2 关庆文;聚丁二酸丁二醇酯拉伸行为及共混改性研究[D];上海交通大学;2010年
3 黄凌燕;石墨烯拉伸性能与尺度效应的研究[D];华南理工大学;2012年
4 夏超;环氧复合材料的界面改性及其环境效应研究[D];燕山大学;2011年
5 马迅;粉煤灰纤维改性及其造纸中纸张抗张强度增强的研究[D];华东理工大学;2012年
6 张若男;夹层玻璃用高性能PVB薄膜的制备和性能研究[D];东华大学;2012年
7 田海霞;超声空化对金属材料力学性能的影响[D];陕西师范大学;2010年
8 吕晓兰;拉应力下2.25Cr1Mo钢中磷的非平衡晶界偏聚[D];哈尔滨工业大学;2010年
9 陈华鑫;叶片挤出机加工的植物纤维/聚丙烯复合材料性能研究[D];华南理工大学;2011年
10 田华;饮用水体系银/壳聚糖类抑菌材料的制备及其性能研究[D];西安建筑科技大学;2011年
 快捷付款方式  订购知网充值卡  订购热线  帮助中心
  • 400-819-9993
  • 010-62982499
  • 010-62783978