Hot Deformation Behavior of 2519 Al Alloy during Isothermal Compression

【摘要】:正The deformation behavior of 2519 aluminum alloy was studied by isothermal compression by Gleeble-1500 simulator in the temperature range from 300 to 450℃ under the strain rates of 0.01-10s-1. The results showed that the flow stress was controlled by strain rate and deformation temperature. The flow stress increased with strain rate and decreased with deformation temperature. The flow stress of 2519 aluminum alloy increased with strain and to the constant values at three strain rates of 0.01 s'-1,0.1 s-1 and 1s-1, indicating the dynamic recovery to occur. The flow stress decreased after a peak value with increase of strain at strain rate 10s-1 and deformation temperature higher than 350℃, showing partly dynamic recrystallization. The flow stress of 2519 aluminum alloy during high temperature deformation can be represented by Zener-Hollomon parameter.
【分类号】:TG146.21;TG172.8

【共引文献】
中国期刊全文数据库 前7条
1 李慧中,张新明,陈明安,周卓平,龚敏如;稀土钇对2519合金组织及耐热性能的影响[J];材料科学与工程学报;2005年01期
2 李慧中,张新明,陈明安,周卓平;热处理制度对2519铝合金晶间腐蚀性能的影响[J];材料热处理学报;2005年01期
3 蒋树农,刘楚明,李慧中,张新明;99.992%高纯多晶铝热压缩流变应力特征[J];热加工工艺;2004年09期
4 吴文祥;孙德勤;张辉;曹春艳;王战锋;;3003铝合金热变形流变应力特征[J];热加工工艺;2007年06期
5 李慧中,张新明,陈明安,周卓平;钇对2519铝合金铸态组织的影响[J];中南大学学报(自然科学版);2005年04期
6 李慧中,张新明,陈明安,周卓平;2519铝合金热变形流变行为[J];中国有色金属学报;2005年04期
7 陈永禄;傅高升;陈文哲;王火生;王沁峰;;经不同熔体处理的易拉罐用铝材的热压缩变形组织[J];中国有色金属学报;2006年01期
中国重要会议论文全文数据库 前4条
1 陈永禄;傅高升;陈文哲;;熔体处理对易拉罐用铝材热变形材料常数的影响[A];福建省科协第五届学术年会数字化制造及其它先进制造技术专题学术年会论文集[C];2005年
2 Gao-yong LIN , Zhen-feng ZHANG , Qi-quan LIN , Da-shu PENG College of Materials Science and Engineering, Central South University, Changsha 410083, China College of Mechanical Engineering, Xiangtan University, Xiangtan 411105, China;The Effects of Thermo-mechanical Treatment on the Properties of 2519 Aluminum Alloy[A];Progress in Light Metals, Aerospace Materials and Superconductors(Part 2----Aluminium Materials)[C];2006年
3 Qiquan LIN1,2,a, Dashu PENG2, Yingming LI1, Gaoyong LIN2 1School of Mechanical Engineering, Xiangtan University, Xiangtan 411105, P.R.China 2School of Materials Science and Engineering, Central South University, Changsha, 410083, P.R.China;A study on the hot deformability of 2519 aluminum alloy at elevated temperature[A];Proceedings of The Fifth International Conference on Physical and Numerical Simulation of Materials Processing[C];2007年
4 熊益民;张永安;朱宝宏;王锋;刘红伟;熊柏青;;Al-Cu-Mg-Ag-Zr合金的热变形研究[A];中国有色金属学会第十二届材料科学与合金加工学术年会论文集[C];2007年
中国硕士学位论文全文数据库 前1条
1 刘友良;V含量对高铜Al-Cu合金组织和性能的影响[D];中南大学;2006年
中国知网广告投放
 快捷付款方式  订购知网充值卡  订购热线  帮助中心
  • 400-819-9993
  • 010-62791813
  • 010-62985026